- Ester & Derivatives[10]
- Oxide[3]
- Polymer[2]
- Silicate[6]
- Titanium Ore[1]
- Chemical Auxiliary Agent[2]
- Daily Chemicals[8]
- Other Electrical Equipment[1]
- Other Inorganic Chemicals[2]
- Other Organic Chemical[1]
- Adhesives & Sealants[1]
- Paraffin[9]
- Pneumatic Parts[7]
- Air-Compressor Parts[1]
- Used General Mechanical Components[1]
- Other Valve Parts[1]
- Valves[1]
- Amine[1]
- Contact Person : Mr. Zhu ChunRong
- Company Name : Zhejiang Taizhou Tu-Poly Co., Ltd.
- Tel : 86-576-88227996
- Fax : 86-576-88227976
- Address : Zhejiang,Taizhou,No.242, Time RD, Taizhou, Zhejiang,China
- Country/Region : China
- Zip : 318000
Fire-Clay And High-Alumina Refractory Castables
Fire-Clay And High-Alumina Refractory Castables
It is the important kind of product among the unshaped refractories. It consists of refractory aggregate, Fine powder and binder. When using it, Installation can be carried out by casting after it is uniformly mixed and then agitated adequately with water. There are three kinds of castables according to the properties of binders i.e. fire clay refractory castables, cement refractory castables and inorganic refractory castables.
Be kept in a dry place.
Items | Fireclay Refractory Castables | Cement Refractory Castables | Inorganic Refractory Castables | ||||||||||||
High Alumina Cement Refractory Castables | Silicate Cement Castables | Phosphate Refractory Castables | Water Glass Castables | ||||||||||||
Brand |
| NL2 | NL1 | NN | G3L | G2L | G2N | G1L | G1N2 | G1N1 | GN | LL2 | LL1 | LN | BN |
Al2O3 | %≥ | 65 | 55 | 45 | 85 | 60 | 42 | 60 | 42 | 30 | 30 | 75 | 60 | 45 | 40 |
Refractoriness | °C ≥ | 1730 | 1710 | 1690 | 1790 | 1690 | 1650 | 1690 | 1650 | 1610 | - | 1770 | 1730 | 1710 | - |
Test Temperature for Reheating Linear Change not Exceeding 1%(After 3hrs at this test temperature) | °C | 1450 | 1350 | 1300 | 1500 | 1400 | 1350 | 1400 | 1350 | 1300 | 1200 | 1450 | 1450 | 1450 | 1000 |
Cold Crushing Strength(After Dry at 105-110°C) | Mpa ≥ | 2.94 | 2.94 | 2.94 | 24.5 | 19.6 | 19.6 | 9.8 | 9.8 | 9.8 | 19.6 | 14.7 | 14.7 | 14.7 | 19.6 |
Moudulus of Rupture(After Dry at 105-110°C) | Mpa ≥ | 0.49 | 0.49 | 0.49 | 0.49 | 3.92 | 3.92 | 3.43 | 3.43 | 3.43 | - | 3.43 | 3.43 | 3.43 | - |
Max,Service Temperature | °C | 1450 | 1350 | 1300 | 1650 | 1400 | 1350 | 1400 | 1350 | 1300 | 1200 | 1600 | 1500 | 1450 | 1000 |
http://www.tu-poly.com/pl-Surfactant-p1.html
Fire-Clay And High-Alumina Refractory Castables